Two-step Synthesis of TiC_(0.7)N_(0.3)@WC-MoC_2 Core-shell Microspheres and Fabrication of TiC_(0.7)N_(0.3)@WC-MoC_2-based Cermets by SPS  

作　　者：俞海军 刘颖 

机构地区：[1]School of Materials Science and Engineering, Sichuan University

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2011年第4期710-714,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National High-tech Research and Development Program of China (2008AA031103);the Scientific and Technical Project of Sichuan Province (07GG002-006)

摘　　要：The precursor with TiC0.7N0.3@WO3-MO3 microspheres were prepared by a novel method from the WO3-MoO3 sol dipping. Subsequently, TiC0.7N0.3@WC-MoC2 core-shell structural microspheres were successfully obtained by carburizing the precursor at 900 °C in a flowing mixture of CH4 （20 ml·min-1） and H2 （200 ml·min-1） for 2 h. Then TiC0.7N0.3@WC-MoC2-15Co cermets were prepared utilizing the core-shell powders by spark plasma sintering （SPS）. Powders of the precursors with TiC0.7N0.3@WO3-MO3 microspheres, TiC0.7N0.3@WC-MoC2 microspheres and TiC0.7N0.3@WC-MoC2-15Co cermets were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and X-ray diffraction （XRD）. The obtained TiC0.7N0.3@WC-MoC2 microspheres have a dense WC-MoC2 coatings shell. The thickness of the shell could be easily controlled by adjusting the number of sol dipping cycles. It was found that the TiC0.7N0.3@WC-MoC2 microspheres were more beneficial to fabricate the ＂core-rim＂ structures by SPS.The precursor with TiC0.7N0.3@WO3-MO3 microspheres were prepared by a novel method from the WO3-MoO3 sol dipping. Subsequently, TiC0.7N0.3@WC-MoC2 core-shell structural microspheres were successfully obtained by carburizing the precursor at 900 °C in a flowing mixture of CH4 （20 ml·min-1） and H2 （200 ml·min-1） for 2 h. Then TiC0.7N0.3@WC-MoC2-15Co cermets were prepared utilizing the core-shell powders by spark plasma sintering （SPS）. Powders of the precursors with TiC0.7N0.3@WO3-MO3 microspheres, TiC0.7N0.3@WC-MoC2 microspheres and TiC0.7N0.3@WC-MoC2-15Co cermets were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and X-ray diffraction （XRD）. The obtained TiC0.7N0.3@WC-MoC2 microspheres have a dense WC-MoC2 coatings shell. The thickness of the shell could be easily controlled by adjusting the number of sol dipping cycles. It was found that the TiC0.7N0.3@WC-MoC2 microspheres were more beneficial to fabricate the ＂core-rim＂ structures by SPS.

关 键 词：core-shell structure spark plasma sintering （SPS） microstructure FABRICATION 

分 类 号：TG148[一般工业技术—材料科学与工程]