焦磷酸钠对镁合金表面磷化膜结构和耐蚀性的影响  被引量:3

Effects of Sodium Pyrophosphate upon Structure and Corrosion Resistance of Phosphating Coating on Magnesium Alloy

在线阅读下载全文

作  者:周勇[1] 胡文娇[1] 李依旋 张丹[1] 江珊[1] 熊金平[1] 

机构地区:[1]北京化工大学教育部碳纤维及功能高分子重点实验室,北京100029 [2]北京碧海舟腐蚀防护工业股份有限公司,北京100029

出  处:《电镀与精饰》2011年第8期5-8,共4页Plating & Finishing

摘  要:通过扫描电镜、极化曲线、电化学阻抗和盐水浸泡等实验研究了焦磷酸钠对镁合金表面磷化膜结构和耐蚀性的影响。实验结果表明:磷化液中加入焦磷酸钠后,镁合金表面磷化膜的结构更加致密和规整;在3.5%的NaCl溶液中,镁合金腐蚀电流密度由2.358×10-5A/cm2下降到1.257×10-5A/cm2、在100mHz下的阻抗值由1.707 kΩ上升到6.129 kΩ,表现出良好的防护性。Effects of sodium pyrophosphate upon structure and corrosion resistance of phosphating coating on magnesium alloy was investigated by scanning electron microscope, polarization curve, electrochemical impedance spectra and salt-water immersion experiment respectively. Results showed that after adding sodium pyrophosphate in the phosphating solution the structure of phosphating coating was more compact and regular; and the corrosion resistance was increased, in 3.5% NaCI solution its corrosion current density from 2. 358 × 10 ^-5A/cm^2decreased to 1. 257 × 10 ^-5/cm^2 and impedance from 1. 707 kΩ increased to 6. 129 kΩ at 100mHz frequency.

关 键 词:镁合金 磷化膜 焦磷酸钠 耐蚀性 

分 类 号:TG174.45[金属学及工艺—金属表面处理]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象