超声振动砂带磨削TiC-TiB_2复合陶瓷的效率研究  

Researches on efficiency of ultrasonic vibration belt grinding of TiC-TiB_2 composite ceramics

作　　者：罗志海[1] 杨润泽[1] 

机构地区：[1]军械工程学院,石家庄050003

出　　处：《金刚石与磨料磨具工程》2011年第4期42-45,共4页Diamond & Abrasives Engineering

基　　金：国家自然科学基金项目资助(51072229)

摘　　要：本文采用超声振动砂带磨削的方法对超重力下燃烧合成的TiC-TiB2复合陶瓷进行磨削试验,寻求提高效率的途径和方法。通过与超声砂轮磨削和普通砂带磨削的对比试验,研究砂带种类、粒度及磨削工艺参数对磨削效率的影响规律,得出当磨削深度0.04 mm,砂带线速度15.2 m/s,工件进给速度1 000mm/min,金刚石砂带粒度60时,材料标准切除率较高。In this paper,ultrasonic vibration belt grinding test was conducted on TiC-TiB2 composite ceramics made by combustion synthesis method under ultra gravity,seeking ways and means to improve the grinding efficiency.In comparison with ultrasonic wheel grinding and common belt grinding without ultrasonic assistance,the effects of diamond grit size and the grinding parameters on the grinding efficiency were analyzed.The results showed that,with grinding depth 0.04 mm,linear speed 15.2 m/s,feed speed 1 000 mm/min and diamond belt grit size 60,the standard material removal of TiC-TiB2 could be increased remarkably.

关 键 词：TiC-TiB2复合陶瓷 超声砂带磨削 效率 

分 类 号：TG58[金属学及工艺—金属切削加工及机床]