直接氮化法制备氮化铝粉末的结构特性  

Structural characteristics of aluminium nitride nanowires synthesized by direct nitridization method

作　　者：马超[1] 陈光德[1] 苑进社[2] 刘菲菲[1] 

机构地区：[1]西安交通大学理学院,陕西西安710049 [2]重庆师范大学物电学院,重庆400047

出　　处：《功能材料》2011年第9期1599-1600,1605,共3页Journal of Functional Materials

基　　金：国家自然科学基金资助项目(11074200);陕西省自然科学基金资助项目(2009JM1005)

摘　　要：用金属镁(Mg)作催化剂,氮气和铝块为反应物,采用直接氮化法制备出氮化铝(AlN)粉末样品。运用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和拉曼光谱仪(Raman)对样品进行结构特性分析发现,AlN样品为纯六方相结构,呈现纳米线堆积形貌,纳米线直径约60nm,且尺寸均匀。拉曼散射光谱峰值较单晶AlN向低波数方向移动,表明此方法制备的AlN纳米线存在表面拉应力。Aluminum nitride（AlN） nanowires were successfully synthesized by direct nitridization method.At 800℃,the reaction of nitrogen and aluminium lump occurred in ordinary equipments with magnesium powder as catalyst.The characterization of samples was done using XRD,SEM and Raman spectrograph.The results reveal the samples were pure hexagonal phase AlN of nanowires heaped structure with diameter about 60nm.The peaks of the Raman spectrum move towards low wavenumbers compared with monocrystal AlN,which demonstrates there is tensile stress in the materials.

关 键 词：氮化铝 纳米线 直接氮化法 金属催化 

分 类 号：TN204[电子电信—物理电子学]