无压浸渗法制备SiC_P/Al复合材料的性能  

Properties of SiC_P/Al Composite Prepared by Pressureless Infiltration

作　　者：张家斯[1] 张萌[1] 

机构地区：[1]南昌大学教育部发光材料与器件工程研究中心,江西南昌330031

出　　处：《热加工工艺》2011年第16期87-89,共3页Hot Working Technology

基　　金：教育部长江学者和创新团队发展计划资助项目(IRT0730)

摘　　要：采用无压浸渗法制备了SiCP/Al复合材料,自氧化法处理的预制型的抗压强度大幅提高,同时降低了该复合材料的残余孔隙率;基体合金中的Mg含量对复合材料的残余孔隙率有较大影响,进而影响了其抗压强度。实验结果表明,采用不同粒径的SiC颗粒配比及自氧化法处理的孔隙率为40%的SiC预制型,无压浸渗Al-11wt%Si-6wt%Mg所制备的SiCP/Al复合材料的抗压强度为367 MPa、热膨胀系数为9.2×10-6/℃。SiCp/Al composite was prepared by prcssurvlass infiltration. The pre-oxidation of SiC particles by high purity oxygen can add a thin layer of SiO2 into-the silicon carbide which can increase the compressive strength of SiC performs and enhance the porosity of the composite. The content of Mg in matrix has an obvious effect on the porosity of the composites, and also has an impact on the compressive strength of the composite. The results show that the compressive strength of the composite, which is obtained by infiltrating AI-I lwt%Si-6wt%Mg alloy into the artificial pre-oxidation preform with 40% porosity, and can reach 367 MPa; the coefficient of the thermal expansion of the composite can reach 9.2×10-6/℃.

关 键 词：SICP/AL 无压浸渗 力学性能 热物理性能 

分 类 号：TB333[一般工业技术—材料科学与工程]