残余V元素对1Cr18Ni9Ti钢板组织与性能的影响  

The effect of residual V on the microstructure and properties in 1Cr18Ni9Ti plate

作　　者：李许明[1] 宋玺玉[1] 马凤春[1] 王晓轩[1] 李凯峰[1] 闫磊[1] 

机构地区：[1]中航工业沈阳黎明航空发动机集团有限责任公司,辽宁沈阳110043

出　　处：《沈阳航空航天大学学报》2011年第4期37-41,共5页Journal of Shenyang Aerospace University

摘　　要：通过试验详细论述了1Cr18Ni9Ti钢中不同残余V含量对材料固溶状态的组织及400℃、500℃长期时效后对组织、晶间腐蚀和室温、高温性能的影响。从而得出结论适量V的存在对1Cr18Ni9Ti钢板组织影响不大,对抗晶间腐蚀性能稍有提高,对室温、高温抗拉强度、屈服强度稍有提高,塑性稍有降低。In this article, we discuss the effect of different residual V contents in 1Crl8Ni9Ti steel on solid solution state organizations, the microstructure, the intergranular corrosion, and the performance under room temperature and high temperature after long-term aging in 400~C or 500~C. The conclusion is that the proper amount of V in 1Crl8Ni9Ti steel has little effect on its organization, with its performance against in- tergranular corrosion, room temperature and high temperature tensile strength, and yield strength slightly in- creasing, and plastic slightly lower.

关 键 词：V含量 时效 固溶 板材 组织性能 

分 类 号：TG174.4[金属学及工艺—金属表面处理]