Ti-V基多相合金的高温电化学性能和反应机制(英文)  

Electrochemical Properties and Reaction Mechanism of Ti-V Multiphase Alloy at High Temperature

作　　者：王宁[1] 柴玉俊[1] 

机构地区：[1]河北师范大学,河北石家庄050016

出　　处：《稀有金属材料与工程》2011年第9期1519-1521,共3页Rare Metal Materials and Engineering

基　　金：National Natural Science Foundation of China(50901030)

摘　　要：研究333K时Ti0.17Zr0.08V0.35Cr0.1Ni0.3合金的循环稳定性和高温倍率放电性能。333K时,当放电电流密度为60mA/g时,Ti0.17Zr0.08V0.35Cr0.1Ni0.3合金第1次放电容量为450mAh/g。随着充放电循环的进行,放电容量迅速降低。当放电电流密度为2400mA/g,截止电压为0.6V时,Ti0.17Zr0.08V0.35Cr0.1Ni0.3合金的放电容量仍达到160mAh/g。并详细探讨影响以上合金电化学性能的因素。The cyclic stability and the high-rate discharge characteristic of Ti0.17Zr0.08V0.35Cr0.1Ni0.3 alloy at 333 K were investigated. The results show that the discharge capacity of Ti0.17Zr0.08V0.35Cr0.1Ni0.3 alloy is ~450 mAh/g at a current density of 60 mA/g at 333 K for the first cycle,and then it obviously decreases with increasing of cycle number. It should be noted that the excellent discharge capacity of Ti0.17Zr0.08V0.35Cr0.1Ni0.3 alloy will remain 160 mAh/g at a current density of 2400 mA/g to cut-off voltage of 0.6 V. Moreover,the possible factors affecting the electrochemical performance of this alloy were discussed.

关 键 词：合金 电化学性能 金属氢化物电极 

分 类 号：TG146.23[一般工业技术—材料科学与工程]