扩散焊制备铜铝复合板的组织性能研究  

Study on Microstructure and Properties of Composite Plate of Copper and Aluminum Alloy Manufactured by Diffusion Welding

作　　者：刘峰[1] 黄华[1] 王云[1] 

机构地区：[1]湖北汽车工业学院材料工程系,湖北十堰442002

出　　处：《热加工工艺》2011年第17期149-151,共3页Hot Working Technology

摘　　要：采用真空扩散焊工艺方法制备铜铝复合板,对加热温度、保温时间、压力等焊接工艺参数对接头组织性能的影响进行正交试验,利用扫描电镜对焊接过渡区的性能进行了分析。试验结果表明:加热温度为540℃、保温时间为60min、压力为4×105MPa时,形成了良好的焊接接头,达到冶金结合。The composite plate of copper and aluminum alloy were manufactured by diffusion welding,and the effect of heating temperature,holding time and pressure on the microstructure and properties of the welded joint were studied by SEM and orthogonal experiments.The experimental results show that the optimal parameters are heating at 540 ℃,holding time 60 min and pressure 4×105 MPa,the welded joints are the metallurgical combination.

关 键 词：扩散焊 铜/铝复合板 组织性能 