甲基丙烯酸-β-羟乙酯磷酸酯的合成及应用  

Synthesis and Application of Phosphoric Acid Methacryloyloxyethyl Ester

作　　者：陈凌霞[1,2] 周晓东[2] 

机构地区：[1]郑州师范学院化学系,450044 [2]华东理工大学化学工程联合国家重点实验室,上海200237

出　　处：《上海涂料》2011年第9期11-14,共4页Shanghai Coatings

摘　　要：以甲基丙烯酸-β-羟乙酯(HEMA)和五氧化二磷(P2O5)为原料,合成了甲基丙烯酸-β-羟乙酯磷酸酯(PMOE)。研究了P2O5用量、反应温度和加水条件等对PMOE中单酯和双酯含量的影响。用已合成的少量PMOE作为分散剂,反应温度75℃,n(HEMA)∶n(P2O5)=2.08∶1.00时,可制备双酯含量为70%以上的PMOE。以PMOE和乙酸铜反应,制备了透明的Cu(Ⅱ)-PMOE金属配合物,与甲基丙烯酸甲酯(MMA)共聚,可得到用途广泛的紫外-近红外吸收透明聚合物材料。A phosphoric acid methacryloyloxyethyl ester was synthesized by β-hydroxyethyl methacrylate （ HEMA ） and phosphorus pentoxide （ P2O5 ）. The effect of the amount of P2O5, reaction temperature and water adding condition on monoester and diester content of PMOE were studied. The PMOE that diester content more than 70% was prepared with reaction conditions such as synthetic PMOE as a dispersant, reaction temperature is 75℃ and n（HEMA） ： n（p2o5） = 2.08 ： 1.00. The uhraviolet-near-infrared absorption transparent copolymer can be prepared by copolymerization MMA and Cu （ Ⅱ ）-PMOE metal complex that prepared with copper acetate and PMOE.

关 键 词：甲基丙烯酸-β-羟乙酯磷酸酯 铜有机配合物 共聚 紫外-近红外吸收透明材料 

分 类 号：TQ265.1[化学工程—有机化工]