Synthesis and Photocatalytic Property of the ZrO_2/TiO_2 Pillared Laponite  

作　　者：林英光 

机构地区：[1]College of Materials Science and Engineering,South China University of Technology

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2011年第5期852-856,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by China Postdoctoral Science Foundation (No.20090450868)

摘　　要：The ZrO2/TiO2 pillared laponite （Ti-Zr-lap） photocatalysts were prepared with intercalation reaction by supercritical fluid drying （SCFD）,and characterized by XRD,TEM,SEM and BET surface area analysis,and the photocatalytic properties of Ti-Zr-lap were investigated by degradation of azo dye acid red B （ARB）.The results showed that the ZrO2/TiO2 pillared structures in laponite could be formed,with the mass fraction of （Zr4＋＋Ti4＋）/laponite （Xm） increasing,the basal spacing and the BET surface area of Ti-Zr-lap significantly increased.The Ti-Zr-lap used as photocatalyst had the advantages of stable and porous layered structure,large surface area with the anatase type TiO2.Compared with the Ti-Zr-lap dried by air drying,the Ti-Zr-lap dried by SCFD showed better photocatalytic property which was very close to that of P25 TiO2.Using the Ti-Zr-lap as photocatalyst with the optimum Xm of 0.16 and the calcination temperature of 500 ℃,under the conditions of the initial concentration of ARB 20 mg/L,photocatalyst concentration of 1.5 g/L and irradiation time 60 min,the decoloring rate of ARB could achieve 98.3%,indicating that the Ti-Zr-lap had excellent photocatalytic property.The ZrO2/TiO2 pillared laponite （Ti-Zr-lap） photocatalysts were prepared with intercalation reaction by supercritical fluid drying （SCFD）,and characterized by XRD,TEM,SEM and BET surface area analysis,and the photocatalytic properties of Ti-Zr-lap were investigated by degradation of azo dye acid red B （ARB）.The results showed that the ZrO2/TiO2 pillared structures in laponite could be formed,with the mass fraction of （Zr4＋＋Ti4＋）/laponite （Xm） increasing,the basal spacing and the BET surface area of Ti-Zr-lap significantly increased.The Ti-Zr-lap used as photocatalyst had the advantages of stable and porous layered structure,large surface area with the anatase type TiO2.Compared with the Ti-Zr-lap dried by air drying,the Ti-Zr-lap dried by SCFD showed better photocatalytic property which was very close to that of P25 TiO2.Using the Ti-Zr-lap as photocatalyst with the optimum Xm of 0.16 and the calcination temperature of 500 ℃,under the conditions of the initial concentration of ARB 20 mg/L,photocatalyst concentration of 1.5 g/L and irradiation time 60 min,the decoloring rate of ARB could achieve 98.3%,indicating that the Ti-Zr-lap had excellent photocatalytic property.

关 键 词：ZrO2/TiO2 pillared laponite photocatalytic property intercalation reaction supercritical fluid drying 

分 类 号：O643.36[理学—物理化学]