ZG30Cr钢铸渗层组织和耐磨性研究  

Microstructure and Wear Resistance of Casting-penetrated ZG30Cr Steel

作　　者：王爱琴[1] 王书利[1,2] 谢敬佩[1] 王文焱[1] 

机构地区：[1]河南科技大学材料科学与工程学院,河南洛阳471003 [2]河南省有色金属材料科学与加工技术重点实验室,河南洛阳471003

出　　处：《热处理》2011年第5期33-36,共4页Heat Treatment

基　　金：河南省国际科技合作项目(项目编号:084300510006);河南科技大学博士科研基金(项目编号2008bs025)

摘　　要：采用铸渗工艺在ZG30Cr钢表面获得了由WC颗粒与高铬铸铁组成的铸渗层。研究了不同WC含量渗层的耐磨性。结果表明,铸渗层致密,无气孔、夹渣等缺陷,与基体为冶金结合,最高表面硬度达820 HV。含15%WC的铸渗层的耐磨性最佳,是基体的18.8倍。Case composed of granular WC and high-chromium casting iron on ZG30Cr steel was developed by a casting-penetrating procedure.Wear resistance of casting-penetrated cases with different quantities of WC was investigated.The results show that the case is dense and free of defects such as pore and slag,and is combined metallurgically with the matrix,and that the highest surface hardness is high as 820 HV.Besides,the case containing 15%WC shows the optimum wear resistance 18.8 times as great as that of the matrix. Key wodrs： casting-penetrating;WC;wear resistance

关 键 词：铸渗 WC 耐磨性 

分 类 号：TG174.445[金属学及工艺—金属表面处理]