双酚A型苯并二噁嗪树脂粘接性能研究  

Study on bonding properties for bisphenol A benzoxazine resin

作　　者：王青松[1] 宁荣昌[1] 艾静[1] 

机构地区：[1]西北工业大学理学院应用化学系,陕西西安710129

出　　处：《中国胶粘剂》2011年第10期10-13,共4页China Adhesives

摘　　要：以环氧树脂(EP)、双马来酰亚胺(BDM)作为纯双酚A型苯并二噁嗪(BA-a)树脂的改性共聚单体,研究了不同改性BA-a体系的粘接性能和热稳定性能。结果表明:纯BA-a树脂与钢材之间的拉伸剪切强度为15.34 MPa,说明纯BA-a树脂具有作为胶粘剂的潜力;当m(BA-a)∶m(EP)∶m(BDM)=100∶60∶0或100∶27∶27时,改性BA-a体系的拉伸剪切强度为24.81 MPa或21.36 MPa,160℃时凝胶时间为150 min或20 min;改性BA-a体系的热稳定性能依次为BA-a/甲基四氢苯酐体系>BA-a/EP体系>BA-a/BDM体系>纯BA-a体系。With epoxy resin（EP） and bismaleimide （BDM） as modified comonomers of pure BA-a（bisphenol A benzoxazine） resin,the bonding properties and thermal stabilities of different modified BA-a systems were investigated. The results showed that the pure BA-a resin had a potential as adhesive because the tensile shear strength between pure BA-a resin and＇steel was 15.34 MPa. The tensile shear strength of modified BA-a system was 24.81 MPa or 21.36 MPa,gelation time was 150 min or 20 min at 160℃ when mass ratio of m （BA-a） ：m （EP） ：m （BDM） was 100：60：0 or 100：27：27. The thermal stabilities of modified BA-a systems were BA-a/MeTHPA system〉 BA-MEP system〉 BA-a/BDM system〉pure BA-a system.

关 键 词：环氧树脂 苯并噁嗪 双马来酰亚胺 结构胶 

分 类 号：TQ436.2[化学工程] TQ323.1