超声振动辅助混粉电火花表面强化试验研究  

Investigation on Ultrasonic Vibration Assisted Powder-mixed Electrical Discharge Surface Modification

作　　者：宋夕超[1] 张建华[1] 董春杰[1] 

机构地区：[1]山东大学机械工程学院高效洁净机械制造教育部重点试验室,山东济南250061

出　　处：《电加工与模具》2011年第5期21-25,共5页Electromachining & Mould

摘　　要：通过对超声振动辅助混粉电火花表面进行的强化试验,分析脉冲宽度、脉冲间隔、脉冲峰值电流、混粉浓度和超声振动振幅等因素对强化层形成的影响规律,并对强化层性能进行研究。结果表明,超声振动辅助混粉电火花表面强化形成的强化层在硬度和耐磨性等方面得到明显提高,强化层厚度可达10μm左右,可有效提高强化处理表面的性能和使用寿命。In this paper, orthogonal experiments of ultrasonic vibration assisted powder-mixed electrical discharge surface modification were finished. The influence of processing parameters, such as pulse duration, pulse interval, peak current, mixed-powder concentration and ultrasonic vibration am- plitude on the formation of strengthen layer by ultrasonic vibration assisted powder-mixed electrical discharge surface modification in kerosene was investigated, and the performance of strengthen layers was tested. Research results show that the performance of modification layer such as micro-hardness, wear resistance was improved obviously, and its thickness is about ten micrometers.

关 键 词：超声振动 混粉电火花 碳化钛 表面强化 

分 类 号：TG661[金属学及工艺—金属切削加工及机床]