层状双金属氢氧化物/壳聚糖复合膜的制备与性能研究  

Study on the Preparation and Properties of M-LDHs/Chitosan Hybrid Films

作　　者：郭丽[1] 王家俊[2] 樊春艳[1] 刘幸幸[1] 

机构地区：[1]浙江理工大学材料与纺织学院,杭州310018 [2]浙江理工大学先进纺织材料与制备技术教育部重点实验室,杭州310018

出　　处：《浙江理工大学学报（自然科学版）》2011年第6期860-864,共5页Journal of Zhejiang Sci-Tech University(Natural Sciences)

摘　　要：用改性层状双金属氢氧化物(M-LDHs)与壳聚糖(CS)溶液共混,制得了具有阻隔性的可降解M-LDHs/CS复合膜。通过X射线衍射、红外光谱和原子力显微镜对复合膜进行结构表征,并对复合膜的气体阻隔性能、透光性能与拉伸性能进行了测试。结果表明:当w(M-LDHs)∶w(CS)为10∶100时,复合膜的氧气阻隔性能最佳,比纯CS膜提高了42%;当w(M-LDHs)∶w(CS)为15∶100时,拉伸强度最大,而断裂伸长率却有所下降。Modified layered double hydroxides/chitosan（M-LDHs/CS） hybrid films are prepared by cosolution method, which is a kind of degradable barrier films. The structure of the films is characterized by XRD, FT-IR and AFM, the gas barrier, optical, and mechanical properties of films are tested. The results show that the oxygen barrier property is best when the w（M-LDHs） ： w（CS） is 10 ： 100, which has been raised 42 % compared with pure chitosan film; the tension strength is up to the maximum when the w（M- LDHs） = w（CS） is 15 ＂. 100, but the breaking elongation is declined.

关 键 词：壳聚糖 M-LDHs 结构 阻隔性能 力学性能 

分 类 号：TB484.6[一般工业技术—包装工程]