In-situ UV-Raman study on soot combustion over TiO_2 or ZrO_2-supported vanadium oxide catalysts  

作　　者：WACHS Israel E. 

机构地区：[1]In-situ Molecular Characterization and Catalysis Laboratory,Department of Chemical Engineering,Lehigh University,Bethlehem,PA 18015,USA

出　　处：《Science China Chemistry》2008年第6期551-561,共11页中国科学（化学英文版）

基　　金：the National Natural Science Foundation of China(Grant Nos.20473053,20773163 and 20525621);the Beijing Natural Science Foundation(Grant No.2062020);the 863 Program of China(Grant No.2006AA06Z346)

摘　　要：UV-Raman spectroscopy was used to study the molecular structures of TiO2 or ZrO2-supported vana-dium oxide catalysts.The real time reaction status of soot combustion over these catalysts was de-tected by in-situ UV-Raman spectroscopy.The results indicate that TiO2 undergoes a crystalline phase transformation from anatase to rutile phase with the increasing of reaction temperature.However,no obvious phase transformation process is observed for ZrO2 support.The structures of supported va-nadium oxides also depend on the V loading.The vanadium oxide species supported on TiO2 or ZrO2 attain monolayer saturation when V loading is equal to 4(4 is the number of V atoms per 100 support metal ions).Interestingly,this loading ratio(V4/TiO2 and V4/ZrO2) gave the best catalytic activities for soot combustion reaction on both supports(TiO2 and ZrO2).The formation of surface oxygen com-plexes(SOC) is verified by in-situ UV Raman spectroscopy and the SOC mainly exist as carboxyl groups during soot combustion.The presence of NO in the reaction gas stream can promote the pro-duction of SOC.UV-Raman spectroscopy was used to study the molecular structures of TiO2 or ZrO2-supported vana-dium oxide catalysts.The real time reaction status of soot combustion over these catalysts was de-tected by in-situ UV-Raman spectroscopy.The results indicate that TiO2 undergoes a crystalline phase transformation from anatase to rutile phase with the increasing of reaction temperature.However,no obvious phase transformation process is observed for ZrO2 support.The structures of supported va-nadium oxides also depend on the V loading.The vanadium oxide species supported on TiO2 or ZrO2 attain monolayer saturation when V loading is equal to 4(4 is the number of V atoms per 100 support metal ions).Interestingly,this loading ratio(V4/TiO2 and V4/ZrO2) gave the best catalytic activities for soot combustion reaction on both supports(TiO2 and ZrO2).The formation of surface oxygen com-plexes(SOC) is verified by in-situ UV Raman spectroscopy and the SOC mainly exist as carboxyl groups during soot combustion.The presence of NO in the reaction gas stream can promote the pro-duction of SOC.

关 键 词：VANADIUM OXIDE catalyst UV-Raman IN-SITU SOOT combustion 

分 类 号：O643.36[理学—物理化学]