高碳钢线材中夹杂物形貌及控制研究  

RESEARCH ON THE FIGURE AND CONTROL OF INCLUSIONS IN WIRE OF HIGH-CARBON STEEL

作　　者：王松昌[1] 苏晓峰[1] 郜拥军[1] 宋万平[1] 

机构地区：[1]安阳钢铁集团有限责任公司

出　　处：《河南冶金》2006年第S1期133-136,共4页Henan Metallurgy

摘　　要：优质高碳钢中的夹杂物来源于脱氧产物、吹氩降温过程中的二次氧化、钢包到中间包浇注过程的二次氧化、钢包和中间包耐火材料的剥离等。指出夹杂物形貌和能谱特征,分析不同破裂指数的夹杂物对线材的影响,为了得到塑性的MnO-Al2O3-SiO2夹杂物,应该采用Si-Mn脱氧。提出生产高碳钢线材过程中减少夹杂物的关键措施。Inclusions of high quality high carbon steel come from deoxidizing production,secondary oxidization in the course of blowing argon and cooling,secondary oxidization during pouring from molten steel container to middle container,refractory peeling of molten steel container and middle container,etc.Inclusion figure and spetrum characteristics are pointed out and the effects of inlusions with different breaking exponent on property of wire rod are analyzed.In order to obtain plasticity MnO-Al2O3-SiO2 inclusion,Si-Mn deoxidization should be adopted.Key measures to decrease inclusion are put forward during producing high carbon steel.

关 键 词：高碳钢 夹杂物 来源 控制 

分 类 号：TF7614[冶金工程—钢铁冶金]