Sol-Gel法制备纳米二氧化钛凝胶的工艺优化  

Optimization of nano-meter TiO_2 powders preparation by Sol-Gel

作　　者：陈建军[1] 陈晓春[1] 李庆余[1] 李吉力[1] 刘业翔[1] 陈汉东 

机构地区：[1]中南大学冶金科学与工程系,长沙410083 [2]湘潭市南方高新技术研究院,湘潭411100

出　　处：《中国有色金属学报》2000年第S1期84-87,共4页The Chinese Journal of Nonferrous Metals

基　　金：教育部博士点基金;教育部优秀青年教师基金!资助项目 ( 1 998年度 )

摘　　要：以钛酸丁酯为前驱物、无水乙醇为溶剂 ,在不同反应条件下研究了Sol Gel法制备纳米二氧化钛光催化剂的胶凝过程。得到了制备稳定溶胶的最佳工艺条件 :前驱物水解是在混合水溶液中进行 ,其混合液由无水乙醇、水和 pH调节剂 (HCl或NH3·H2 O)组成 ,并采用滴加式加入 ;钛醇盐与水的摩尔比取 2～ 3;乙醇与钛醇盐摩尔比m取 5～ 8;pH值取 1～ 2 ;水解温度为 2 0～ 40℃。The preparation of TiO_2 by Sol-Gel method was studied under different conditions using Ti(OBu)_4 as presursor and C_2H_5OH as solvent. The optimum preparation conditions are as follows. Hydrolysis of Ti(OBu)_4 is finished in a mixture made of alcohol, water and pH regulators (HCl or NH_3·H_2O), the affusion way of solution is ditration. The molar ratio of Ti(OBu)_4 to water is 2～3. The molar ratio of alcohol to Ti(OBu)_4 is 5～8. The pH value of the solution is 1～2. Hydrolysis temperature is 20～40 ℃.

关 键 词：光催化 纳米二氧化钛粉末 胶凝 