Structure of the Intermetallic Compound Ni_3Al Synthesized under Compression of the Powder Mixture of Pure Elements Part Ⅱ: Influence of Alloying by Boron on the Phase Composition and the Microstructure of Grains of the Main Phase  

作　　者：M. V.Fedorischeva, V.E.Ovcharenko,O.B.Perevalova and E.V.Kozlov (Institute of Strength Physics and Materials Science, Russian Academy of Sciences, Siberian Branch.Tomsk, Russia) 

出　　处：《Journal of Materials Science & Technology》2000年第1期15-18,共4页材料科学技术（英文版）

摘　　要：The Ni_3B phase was formed when boron (0.5 at. pct B) was added to the intermetallic of sto- ichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles of Ni_3B phase has the size around 0.1μm and is located on the grain boundary of the main phase. The decreasing of concentrations of Al in the ofF-stoichiometric alloy leads to increase in the degree of the long-range order parameter, increasing the concen- trations of boron in the solid solution and decreasing its localization on the grain boundary. Microalloying of boron leads to increasing in the fraction of grain monodomains with disloca- tions up to 0.7 in the alloy of the off-stoichiometric composition and up to 1 in the alloy of the stoichiometric composition. It was established the correlation between the degree of the concentration inhomogeneity, average density of the dislocations and the average long range-order parameter.The Ni_3B phase was formed when boron (0.5 at. pct B) was added to the intermetallic of sto- ichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles of Ni_3B phase has the size around 0.1μm and is located on the grain boundary of the main phase. The decreasing of concentrations of Al in the ofF-stoichiometric alloy leads to increase in the degree of the long-range order parameter, increasing the concen- trations of boron in the solid solution and decreasing its localization on the grain boundary. Microalloying of boron leads to increasing in the fraction of grain monodomains with disloca- tions up to 0.7 in the alloy of the off-stoichiometric composition and up to 1 in the alloy of the stoichiometric composition. It was established the correlation between the degree of the concentration inhomogeneity, average density of the dislocations and the average long range-order parameter.

关 键 词：Al Part Structure of the Intermetallic Compound Ni3Al Synthesized under Compression of the Powder Mixture of Pure Elements Ni 

分 类 号：TG146[一般工业技术—材料科学与工程]