A study on welded joint toughness of X-60 steel  

作　　者：姚舜 石忠贤 楼松年 

出　　处：《China Welding》2000年第2期29-35,共7页中国焊接（英文版）

摘　　要：Charpy impact test and COD test were performed on the specimens subjected to simulated welded thermal cycle and the specimens taken from welded joint. The optical microscope, TEM, SEM, EDAX and XRD analysis have been used to investigate the behaviors of second phase particles and the effects of microstructure on toughness separately. The results are as follows. The dispersed second phase particles can effectively retard the growth of austenite grain in the coarse grained HAZ (CGHAZ), and improve the toughness. When t 8/5 is different, the behaviors of the particles are also different in dissolving, coarsening and re precipitating. The ability of retarding the growth of austenite grain will be affected. When t 8/5 increases from 10 s to 70 s , the microstructure of CGHAZ will transform from upper bainite and granular bainite to granular bainite, and the size of austenite grain will grow a little, thus the toughness of the materials decreases slightly.Charpy impact test and COD test were performed on the specimens subjected to simulated welded thermal cycle and the specimens taken from welded joint. The optical microscope, TEM, SEM, EDAX and XRD analysis have been used to investigate the behaviors of second phase particles and the effects of microstructure on toughness separately. The results are as follows. The dispersed second phase particles can effectively retard the growth of austenite grain in the coarse grained HAZ (CGHAZ), and improve the toughness. When t 8/5 is different, the behaviors of the particles are also different in dissolving, coarsening and re precipitating. The ability of retarding the growth of austenite grain will be affected. When t 8/5 increases from 10 s to 70 s , the microstructure of CGHAZ will transform from upper bainite and granular bainite to granular bainite, and the size of austenite grain will grow a little, thus the toughness of the materials decreases slightly.

关 键 词：coarse  grained HAZ cooling time second phase particles toughnesT 

分 类 号：TG142[一般工业技术—材料科学与工程]