Microstructure of YBCO Superconducting Film on Metal Substrate with YSZ Buffer Layer  

作　　者：王敬 刘安生 石东奇 王小平 王晓华 邵贝羚 袁冠森 

出　　处：《Journal of Rare Earths》1998年第1期73-77,共5页稀土学报（英文版）

摘　　要： Microstructures of YBa_2Cu_3O_(7-y)(YBCO) film on flexible metal substrate with yttriastabilized zirconia(YSZ) buffer layer prepared by magnetron sputtering technique have been studied in this paper using transmission electron microscopy(TEM). A critical temperature(Tc) and a critical current density(Jc) of the YBCO film are 91 K and 2×103 A/cm2 at 77 K, 0 T respectively. Bonded steadfastly to the substrate of nickel alloy(HastelloyC), the dense, even and textured YSZ layer with fine crystal grains is about 12 μm thick. With an uneven thickness of about 500 nm, the YBCO layer is sometimes weakbonded to the YSZ layer. Impurities which occasionally led to cracks were observed at the YSZ/YBCO interface. Microstructures of YBa_2Cu_3O_(7-y)(YBCO) film on flexible metal substrate with yttriastabilized zirconia(YSZ) buffer layer prepared by magnetron sputtering technique have been studied in this paper using transmission electron microscopy(TEM). A critical temperature(Tc) and a critical current density(Jc) of the YBCO film are 91 K and 2×103 A/cm2 at 77 K, 0 T respectively. Bonded steadfastly to the substrate of nickel alloy(HastelloyC), the dense, even and textured YSZ layer with fine crystal grains is about 12 μm thick. With an uneven thickness of about 500 nm, the YBCO layer is sometimes weakbonded to the YSZ layer. Impurities which occasionally led to cracks were observed at the YSZ/YBCO interface.

关 键 词：Rare earths YBCO film YSZ buffer layer MICROSTRUCTURE Metal substrate 

分 类 号：O614.33[理学—无机化学]