SOLIDIFICATION MECHANISM OF UNDERCOOLEDSINGLE PHASE ALLOYS  

作　　者：J.F.Li G.C.Yang Y.H.Zhou 

出　　处：《Acta Metallurgica Sinica(English Letters)》1998年第2期100-106,共7页金属学报（英文版）

摘　　要：The solidification behavior of bulk undercooled Ni50Cu50 alloy was systematically investigated. Double recalescences were discovered for the first time in a single phase Ni-Cd alloy, in which there is no solid phase transition at elevated temperature. When the alloy melt was undercoolcd below the solidus temperature, the effect of nonequilibrium solidification could make the solid with the norminal composition C0 of the alloy nucleate and grow till tempemture approached To (the temperuture at which the free enengies of solid and liquid with C0 are equal). Following it, the nucleation and growth of the solid with more high melting point component were required, so the secondary recalescence took place. The concentration distribution in crystals was also analysed.The solidification behavior of bulk undercooled Ni50Cu50 alloy was systematically investigated. Double recalescences were discovered for the first time in a single phase Ni-Cd alloy, in which there is no solid phase transition at elevated temperature. When the alloy melt was undercoolcd below the solidus temperature, the effect of nonequilibrium solidification could make the solid with the norminal composition C0 of the alloy nucleate and grow till tempemture approached To (the temperuture at which the free enengies of solid and liquid with C0 are equal). Following it, the nucleation and growth of the solid with more high melting point component were required, so the secondary recalescence took place. The concentration distribution in crystals was also analysed.

关 键 词：undercooled Ni-Cu alloy secondary recalescence solidification mechanism 

分 类 号：TG13[一般工业技术—材料科学与工程]