加载速率对34CrMo4钢CT试样应力腐蚀行为的影响  

Effect of Loading Rate on Stress Corrosion Cracking Behavior of 34CrMo4 Steel CT Specimens

作　　者：南广利[1,2] 张玮[1,2] 郑三龙[1,2] 陈冰冰[1,2] 高增梁[1,2] 

机构地区：[1]浙江工业大学化工机械设计研究所,浙江杭州310014 [2]浙江工业大学过程装备及其再制造教育部工程研究中心,浙江杭州310014

出　　处：《压力容器》2011年第11期1-7,24,共8页Pressure Vessel Technology

基　　金：国家"863"高技术研究发展计划项目(2009AA044802)

摘　　要：在湿H2S环境下,对34CrMo4高强钢的紧凑拉伸(CT)试样按不同位移速率进行拉伸,并对断口形貌及载荷—位移曲线进行了分析。结果表明,当位移速率在10-5～10-4 mm/s范围内,试样呈脆性断裂,可见明显应力腐蚀现象;当位移速率过快或过慢时,应力腐蚀敏感性会显著降低,试样呈韧性断裂。In wet H2S environment, the tensile curve and fracture mophology of stress corrosion of compact tension （CT） specimens of 34CrMo4 high -strength steel at different constant displacement rates were investigated. The specimens showed brittle fracture and clearly stress corrosion phenomenon when displacement rate was in the extent of 10-5 - 10-4 mm/s. The specimens showed ductile fracture and the stress corrosion sensitivity decreased significantly when displacement rate was too fast or too slow.

关 键 词：紧凑拉伸试样 位移速率 应力腐蚀 断口形貌 

分 类 号：TG172.9[金属学及工艺—金属表面处理] TB302.3[金属学及工艺—金属学]