铝电解槽用自结合碳化硅侧衬材料的性能  

Performance of self-bonded SiC material for aluminium reduction cells

作　　者：黄志明[1] 黄志林[1] 周东方[2] 金景林 王建栋[1] 黄志刚[1] 

机构地区：[1]中钢集团洛阳耐火材料研究院有限公司,先进耐火材料国家重点实验室,河南洛阳471039 [2]沈阳铝镁设计研究院有限公司,辽宁沈阳110001 [3]抚顺铝业有限公司,辽宁抚顺113001

出　　处：《轻金属》2011年第11期37-39,共3页Light Metals

摘　　要：研究分析了以SiC为结合相的自结合碳化硅砖的力学性能、化学组成、热导率及抗冰晶石侵蚀性、抗熔碱侵蚀、抗氧化性、抗热震等使用性能,并与氮化硅结合碳化硅材料进行了对比试验。研究结果表明,自结合碳化硅具有良好的力学性能,抗碱性和抗热震性较氮化硅结合碳化硅更优,热导率比氮化硅结合碳化硅砖高10%～20%,抗冰晶石侵蚀性能比氮化硅结合碳化硅提高近1倍,预计这种新型碳化硅砖作为超大型铝电解槽侧衬更具优势。The mechanical properties,chemical composition and thermal conductivity of self-bonded SiC material as well as its service performances such as cryolite resistance,alkali resistance,oxidation resistance and thermal shock resistance etc were investigated and compared with Si3N4-SiC material.The results showed that self-bonded SiC material presented good mechanical properties and superior alkali resistance and thermal shock resistance to Si3N4-SiC material.Particularly,the thermal conductivity of such material was 15%~25% higher than that of Si3N4-SiC material,with cryolite resistance nearly twice as good.Self-bonded SiC material was of great potential to be used as sidewall block in large-scale aluminium reduction cells.

关 键 词：自结合碳化硅 侧衬材料 大型铝电解槽 

分 类 号：TF821[冶金工程—有色金属冶金]