多孔陶瓷负载TiO_2光催化剂降解亚甲基蓝  

DEGRADATION OF METHYLENE BLUE BY USING TiO_2 PHOTOCATALYST COATED ON POROUS CERAMICS

作　　者：张荔荔[1] 张永明[2] 

机构地区：[1]上海师范大学继续教育学院,上海200234 [2]上海师范大学生命与环境科学学院,上海200234

出　　处：《中国陶瓷》2011年第12期30-34,共5页China Ceramics

基　　金：国家自然科学基金项目(50978164);高等学校博士学科点专项科研基金项目(20070270003);上海市重点学科建设项目(S30406)

摘　　要：以多孔轻质陶瓷作为TiO_2催化剂载体,采用溶胶凝胶方法制备负载型催化剂,比较了不同的煅烧温度条件下TiO_2的晶形变化情况,并将这些催化剂用来降解亚甲基蓝,以比较它们的降解活性。研究结果证明,随着煅烧温度的升高,部分锐钛矿会转变为金红石,从而降低了TiO_2催化剂的活性。紫外照射TiO_2催化剂比自然光照射时,其活性更高。TiO_2 was coated on porous ceramics by sol-gel method to prepare load type TiO_2 photocatalyst. It was compared that crystal form of TiO_2 changes under different calcination temperature.These catalysts were respectively used for degradation of methylene blue in order to compare their activity degrading methylene blue.Experimental results indicated that part anatase was transferred into rutile with increasing of temperature, which decreased TiO_2 catalytic activity.Compared with natural light,UV light had higher catalytic activity.

关 键 词：二氧化钛 催化剂 轻质多孔陶瓷载体 

分 类 号：TQ174.758[化学工程—陶瓷工业]