纯棉织物负离子整理工艺的测试分析  

Test and Analyses on Negative Ions Finishing Processing of Pure Cotton Fabric

作　　者：任彩玲[1] 孟家光[1] 王吉国[1] 

机构地区：[1]西安工程大学

出　　处：《棉纺织技术》2011年第12期31-34,共4页Cotton Textile Technology

基　　金：陕西省重点学科建设专项资金项目资助(陕教资[2008]169)

摘　　要：探讨纯棉织物负离子整理工艺及整理效果。采用电气石超微粉体对织物进行了负离子整理。分析了电气石超微粉体用量、黏合剂用量、浴比、浸渍时间对织物负离子释放性能的影响,通过正交试验对试验工艺参数进行了优选,并对整理后织物的负离子释放性能、耐水洗性、力学性能、透气透湿性进行了测试。结果表明:最佳的纯棉织物负离子整理工艺为电气石超微粉体2.5%(o.w.f.),浸渍时间30 min,焙烘时间2 min,焙烘温度100℃。认为:经优化工艺整理得到的织物具有良好的负离子释放性能及耐水洗性。Negative ions finishing processing and the effect of pure cotton fabric were discussed. Negative ions finishing was carried on pure cotton fabric by tourmaline superfine powder. Effect of amount of tourmaline superfine powder,adhesive amount,bath ratio and dipping time were analyzed. Processing parameter was optimized by orthogonal test. Then fabric negative ions release property, washing property, mechanical property, breathable and water permeability were tested. The result shows that the best finishing processing should be tourmaline superfine powder 2.5% , dripping time 2 min,curing temperature 100 °C. It is considered that better negative ions release property and washing property of the fabric can be got by optimized finishing processing.

关 键 词：负离子整理 电气石超微粉体 浸渍时间 正交试验 服用性能 

分 类 号：TS195.6[轻工技术与工程—纺织化学与染整工程]