连铸板坯宽面边部纵向凹陷的预防  

Prevention of Longitudinal Off-Corner Drepression in Continuously Cast Steel Slabs

作　　者：鲁永剑[1] 王谦[1] 李玉刚[1] 何生平[1] 

机构地区：[1]重庆市冶金工程重点实验室重庆大学材料科学与工程学院,重庆400045

出　　处：《连铸》2011年第6期33-37,共5页Continuous Casting

摘　　要：国内钢厂连铸板坯生产过程中,铸坯宽面边部纵向凹陷频发,严重时影响了连铸坯的表面质量,并造成轧材缺陷。主要分析了连铸板坯宽面边部纵向凹陷的形成原因,讨论了影响边部纵向凹陷产生的因素。结合生产现场试验,通过优化结晶器流场、优化结晶器锥度以及加强结晶器足辊段窄面的冷却强度等一系列有效的措施,使连铸板坯宽面边部纵向凹陷得到了有效的预防,连铸坯表面质量显著改善。The longitudinal off-corner depressions in continuously cast steel slabs were observed frequently during production in some iron and steel companies.The main causes for the problem and influence factors were discussed; and the prevention methods based on the practice were put forward.As a result,the surface quality of slabs were improved significantly through optimization of mold flow pattern,modification of mold taper and enhancement of narrow face sprays just below the mold.

关 键 词：铸坯表面质量 边部纵向凹陷 成因分析 预防措施 

分 类 号：TF777[冶金工程—钢铁冶金]