引线框架用KFC铜合金低温形变热处理后的组织与性能  

Microstructure and Properties of KFC Copper Alloy Used for Lead Frame after Low Temperature Thermo-Mechanical Treatment

作　　者：黄鑫[1,2] 王德志[1] 曾菊花[1] 林高用[1] 

机构地区：[1]中南大学材料科学与工程学院,长沙410083 [2]广州铜材厂有限公司,广州510990

出　　处：《机械工程材料》2011年第12期59-62,共4页Materials For Mechanical Engineering

基　　金：国家科技支撑计划项目(2007BAE38BO4)

摘　　要：对引线框架用KFC铜合金板坯在固溶处理后进行冷轧变形,然后分别在500,400℃两次时效处理间实施不同变形量的冷轧变形,采用光学显微镜、TEM、力学性能试验机和电导率测试仪等研究了低温形变热处理对KFC铜合金组织和性能的影响。结果表明:随着两次时效之间的冷轧变形量从0%增加到90%,合金的位错增殖越明显,第二相析出越充分;当冷轧变形量为75%时,铜合金可获得最佳的综合性能,其抗拉强度达到417 MPa,硬度达到126 HV,伸长率达到11%,电导率达到91.2%IACS,并具有良好的热稳定性。The KFC copper alloy plates used for lead frame were cold rolled after solid solution, then cold rolling with different deformation were done between the two aging treatments at 500℃ and 400℃ respectively. The effect of the low temperature thermo-mechanical treatment on the microstructure and properties of the alloy was studies by means of optical microscopy, TEM, mechanical property test machine and conductivity analyzer. The results show that with increase of cold rolling deformation between the aging treatments from 0% to 90%, the dislocation increment of the alloy was more obviously and the precipitation of second phase was more sufficient. When the cold rolling deformation was 75%, the alloy had optimal comprehensive properties, the tensile strength was 417 MPa, the hardness was 126 HV, the elongation was 11%, the conductivity was 91.2% IACS, and its thermal stability was good.

关 键 词：KFC铜合金 引线框架 低温形变热处理 

分 类 号：TG156.93[金属学及工艺—热处理]