废轮胎胶粉/SBS复合改性沥青制备工艺优化研究  

Research on Optimization of Crumb Rubber/SBS Complex Modified Asphalt Preparation Technology

作　　者：丁红霞 程国香[2] 张建峰[2] 

机构地区：[1]辽宁石油化学大学,抚顺113001 [2]抚顺石油化工研究院,抚顺113001

出　　处：《石油沥青》2011年第6期25-29,共5页Petroleum Asphalt

摘　　要：摘要:以"东海牌"70号A级沥青为基质沥青,加入80目废轮胎胶粉和SBS制备复合改性沥青。用均匀设计法考察了胶粉/SBS复合改性沥青制备的影响因素。根据均匀设计软件分析,最佳工艺条件为:胶粉加入量小于等于10%,加工温度180～200℃,加工时间200～260 min,SBS加入量2.5%～3.5%。试验结果表明,复合改性沥青关键性能满足JTGF40—2004 I-C技术指标。Complex polymer modified asphalts were prepared by adding 80mesh crumb rubber and SBS to Sinopec ＂East Sea＂ penetration 70# Grade A paving asphalt. Influencing parameters of the preparation process were investigated by uiform dsign method.. The results showed that the main indices of the samples could meet I -C technical requirements of JTG F40 -2004 specification, and the optimum processing conditions were as follow： crumb rubber dosage less than 10%, SBS dosage from 2.5% to 3. 5%, reaction temperature from 180℃ to 200 ℃, and reaction time from 200 to 260 min respectively.

关 键 词：废轮胎胶粉 SBS 复合改性 均匀设计 

分 类 号：U414[交通运输工程—道路与铁道工程]