铜对铸态高强度球墨铸铁性能的影响  

Influence of Cu on Properties of High Strength Ductile Cast Iron

作　　者：马晓丽[1] 雷富军[1] 刘俊英[1] 王小红[1] 堀江皓[2] 

机构地区：[1]青海大学机械工程学院,青海西宁810016 [2]日本岩手大学工学部

出　　处：《铸造》2011年第12期1245-1248,共4页Foundry

摘　　要：试验了一种在铸态下得到高强度球墨铸铁的方法。利用稀土的石墨化作用,再添加一定量的碳化物形成元素锰,珠光体稳定化元素铜,使薄壁球墨铸铁不产生白口,基体组织为微细全珠光体,从而得到高强度球墨铸铁。试验结果表明:铜添加量为1.5%的Y型试样,其抗拉强度超过900 MPa,伸长率为4%左右;铜添加量为1.5%的Φ10 mm试样,其抗拉强度接近1 100 MPa,伸长率为7%左右。The high strength thin walled ductile cast iron with no chill was produced by adding a certain amount of carbide forming element Mn and pearlite stabilizing element Cu, and its structure is all fine pearlite. The experimental results show that with 1.5% Cu addition the Y-shape sample has a tensile strength more than 900 MPa and an elongation of about 4%; while for the bar sample of φ10 mm, its tensile strength is close to1 100 MPa and elongation is around 7%.

关 键 词：高强度球墨铸铁 白口化倾向 珠光体 

分 类 号：TG255[金属学及工艺—铸造]