二元酸盐聚丙烯β晶型成核剂的制备及性能  

Preparation and Properties of the Dicarboxylate Polypropylene β-Nucleating Agent

作　　者：吕志平[1] 徐美玲[1] 万兆荣[1] 王卫星[1] 

机构地区：[1]太原理工大学精细化工研究所,山西太原030024

出　　处：《高分子材料科学与工程》2011年第12期110-113,共4页Polymer Materials Science & Engineering

摘　　要：利用邻苯二甲酸酐,甘氨酸和氢氧化钙制备了新型结构成核剂——N-甘氨酸基苯甲酰氨酸钙(PGCa)。利用TGA考察了其热稳定性,采用X射线衍射分析(XRD)和偏光显微镜(PLM)对其改性聚丙烯的结晶形态进行了表征,用差示扫描量热法(DSC)研究了其结晶行为,并测试了其力学性能。结果表明,PGCa是一种有效的β晶型聚丙烯成核剂。当PGCa质量分数为0.15%时,β晶型的相对含量可达74.2%,抗冲击强度由纯PP的12.07 kJ/m2提高到38.13 kJ/m2,拉伸强度和弯曲强度略有降低。Calcium N-glycinylphthalamate（PGCa） was prepared by phthalic anhydride,glycine,and calcium hydroxide.The thermodynamic stability of PGCa and the influence on crystalline morphology and crystallization behavior of PP were studied with thermogravimetry（TGA）,X-ray diffraction（XRD）,polarized opticalmicroscopy（PLM） and differential scanning caloimetry（DSC）,the mechanical properties were also tested.The results show that PGCa is an effective β-form nucleating agent of PP.While the addition of PGCa is 0.15%,the content of β-crystal is 74.2%,and the impact strength of PP is improved from 12.07 kJ/m2 to 38.13 kJ/m2,but the flexural strength and the tensile strength decrease slightly.

关 键 词：聚丙烯 二元羧酸盐 Β晶型成核剂 性能 

分 类 号：O631.13[理学—高分子化学]