石灰烧结法从煤系高岭土提取氧化铝的研究  

Technology Process of Extraction of Alumina from Coal-measures Kaoline by Sintering Method of Limestone

作　　者：任根宽[1] 朱登磊[1] 

机构地区：[1]宜宾学院化工系,四川宜宾644007

出　　处：《非金属矿》2012年第1期7-9,共3页Non-Metallic Mines

摘　　要：采用高岭土为原料提取氧化铝,研究以萤石为助剂煅烧活化煤系高岭土和溶出提取氧化铝的条件,考察了煤系高岭土煅烧活化和溶出条件对煤系高岭土中氧化铝溶出率的影响。实验表明,煅烧活化条件为:石灰石与煤系高岭土质量比2.5、萤石用量1%、煅烧温度1260℃、烧成时间90 min;溶出的最佳工艺条件为:溶出温度85℃、溶出时间2.0 h、Na2CO3质量分数9%、液固比3.5,在此条件下,粉煤灰中氧化铝的溶出率高达90.5%。Using Kaolin as a raw material to extract alumina. The conditions of calcining activation of fly ash with fluorite as assistant and extracting alumina were studied, the effects of conditions of calcining activation and leaching on the leaching rate of alumina from fly ash were investigated. The experimental results show that the conditions of calcining activation were obtained as： dosage of fluorite 1%, mass ratio limestone to fly ash 2.5, calcination temperature 1260℃, calcination time 90 min; the best technological conditions of leaching were as follows： under liquid-to-solid ratio 3.5, alumina leaching efficiency of 90.5% was achieved when clinker was leached with 9% Na2CO3 at 85 ℃ for 2 h.

关 键 词：煤系高岭土 溶出率 提取 氧化铝 

分 类 号：TD985[矿业工程—选矿]