聚氨酯微孔弹性体的制备及动静刚度比研究  

Preparation and Spring Ratio of Microcellular Polyurethane Elastomer

作　　者：唐功庆[1] 罗玉媛[1] 张梅[1] 潘赏[1] 姜志国[2] 

机构地区：[1]北京化工大学材料科学与工程学院,北京100029 [2]北京化工大学北京市新型高分子材料制备与加工重点实验室,北京100029

出　　处：《橡胶工业》2012年第2期80-83,共4页China Rubber Industry

摘　　要：采用组合聚醚多元醇、二苯基甲烷二异氰酸酯、多亚甲基多苯基多异氰酸酯(PAPI)和1,4-丁二醇制备聚氨酯微孔弹性体(MPUE),并对其动静刚度比进行研究。结果表明:在硬段中加入PAPI可有效降低MPUE的动静刚度比;异氰酸根指数和硬段含量适中时,可制备出动静刚度比较小的MPUE。A microcellular polyurethane elastomer（MPUE） was prepared by using premixed polyether polyol,diphenylmethane-4,4-diisocyanate,polyaryl polymethylene isocyanate（PAPI） and 1,4-butanediol,and its spring ratio was investigated.The results showed that,by using PAPI in hard segment,the spring ratio of MPUE was decreased significantly.When the isocyanate index and mass fraction of hard segment were proper,MPUE with low spring ratio was prepared.

关 键 词：聚氨酯弹性体 微孔 动静刚度比 

分 类 号：TQ334.1[化学工程—橡胶工业]