SWRH82B高碳钢盘条生产实践  

Production practice of SWRH82B high carbon steel wire rod

作　　者：邓保全[1,2] 张全刚[1,2] 范银平[2] 王田丰[2] 

机构地区：[1]北京科技大学,北京100083 [2]安阳钢铁股份有限公司,河南安阳455004

出　　处：《金属制品》2012年第1期39-42,共4页Metal Products

摘　　要：SWRH82B高碳钢盘条主要用于制作高强度低松弛预应力钢丝和钢绞线。采用长短复合流程,优化化学成分,LF炉精炼时间不小于45 min,白渣保持时间不小于15 min;连铸结晶器电磁搅拌频率5 Hz,电流246 A,拉速2.1～2.3 m/min,过热度小于30℃,比水量0.7～0.85 L/kg;轧制温度1 050～1 100℃,开轧温度950～990℃,减定径轧制及吐丝温度880～900℃,辊道速度40～60 m/min。生产的预应力钢绞线用SWRH82B高碳钢盘条,抗拉强度大于1 150 MPa,断面收缩率大于35%,夹杂物的尺寸小于20μm,数量小于6个/mm2,w(N)≤70×10-6,w(O)≤40×10-6,完全满足1 860 MPa级以上钢绞线用盘条的需要。SWRH82B high carbon steel wire rod is mainly used to produce high strength low relaxation prestressed steel wire and steel strand. The chemical composition is optimized by adopting long and short composite process. LF furnace re- fine time is no less than 45 rain, white slag keep time is no less than 15 rain. Continuous casting crystallizer electromagnetic stirring frequency is 5 Hz, current is 246 A, casting speed is 2. 1 - 2. 3 m/min, superheat degree is less than 30 ℃, specific water flow is 0. 7 -0. 85 L/kg. Rolling heating temperature is 1 050 - 1 100℃, open rolling temperature is 950-990 ℃, size reducing rolling and wire laying temperature is 880 - 900℃, roller speed is 40 - 60 m/min, SWRH82B high carbon steel wire rod for prestressed steel strand is produced, tensile strength is higher than 1 150 MPa, area reduction is higher than 35% , inclusion size is smaller than 20 μm, each square millimeter quantity is less than 6, mass fraction of ni- trogen is no more than 70 × 10-6 ,mass fraction of oxygen is no more than 40 × 10-6, which satisfy requirements of higher than 1 860 MPa grade wire rod for steel strand.

关 键 词：SWRH82B 高碳钢 钢绞线 抗拉强度 断面收缩率 

分 类 号：TG335.11[金属学及工艺—金属压力加工]