ZnO-V_2O_5-MnO_2中压体系压敏电阻的微观组织和电学性能  

Microstructure and Varistor Properties of ZnO-V_2O_5-MnO_2-based Medium-voltage Ceramics

作　　者：桑小龙[1] 柳飞[2] 

机构地区：[1]东华大学机械学院,上海201620 [2]同济大学先进土木工程材料教育部重点实验室,上海200092

出　　处：《材料导报》2012年第4期15-17,共3页Materials Reports

基　　金：国家自然科学基金(20901001);安徽省教育厅重点科研项目(KJ2010A064)

摘　　要：研究了中压体系ZnO-V2O5-MnO2(ZVM)压敏电阻的微观组织和电学性能。结果表明,MnO2含量增加有利于细化ZVM陶瓷晶粒,改善电性能,提高压敏电压;提高烧结温度可以促进ZVM陶瓷晶体生长,改善致密度,降低压敏电压,提高非线性系数。中压体系ZVM陶瓷可以通过控制MnO2含量以及烧结温度获得。The effe＇ct of MnO2 and sintering temperature of ZVM-based medium-voltage varistors were investigated. The results indicate that the increase of the content of MnO2 is benefit to refining grains, increase breakdown voltage（VB, be measured at 1.0mA/cm2 ）, increase non-ohomic value（a） amd improve electrical properties. Increasing sinter temperature can promote the grain growth of ZVM-based ceramics, improve density, increase a and reduce VB. Medium-voltage ZVM-based varistor can be acquired through the control of MnO2 and sintering temperature.

关 键 词：氧化锌 压敏电阻 中压 电学性能微观结构 