Adsorbability and preparation of active carbon fiber fabric using phosphoric acid

作　　者：储长流[1] 毕松梅[2] 罗云肖[2] 

机构地区：[1]安徽工程大学安徽省纺织面料重点实验室,安徽芜湖241000 [2]安徽工程大学纺织服装学院,安徽芜湖241000

出　　处：《安徽工程大学学报》2011年第4期36-39,共4页Journal of Anhui Polytechnic University

基　　金：芜湖市科技计划基金资助项目(芜科计字[2006]91号文)

摘　　要：采用磷酸作为活化剂,以优选后的聚丙烯腈预氧化织物为原料制备活性炭纤维布,探讨磷酸质量分数、浸渍时间、活化温度及活化时间等工艺参数对活性炭纤维布吸附性能的影响.结果表明,最适的工艺条件为磷酸质量分数15%～20%、浸渍时间15～25h、活化温度650℃、活化时间30min.形貌表征显示所制备的活性炭纤维布表面产生了很多微孔,有利于吸附各种气体,同时在微孔的边缘,出现白色小颗粒,可能是活化剂磷酸在高温下形成的.With phosphoric acid as activating agent,the Optimal PAN Precursor Preoxidation fabrics was made into ACF cloth.The influences of phosphoric acid concentration,dip time,activating temperature and activating time on the adsorbability of ACF cloth were investigated.The results show that the optimal parameters such as phosphoric acid concentration,the dip time,activating temperature and activating time were 15%~20%,15~25 h,650 ℃ and 30 min respectinvely.Many micropores were produced on the ACF cloth surface,which contributed to the adsorption of various gases.At the same time,some miniscule particles existed at the edge of the micropores,which was probably caused by activating agent with high temperature.

关 键 词：磷酸 活化 活性炭纤维布 制备 吸附性 

分 类 号：TS102.6[轻工技术与工程—纺织工程]