基于CSP工艺热轧及冷轧过程3%Si钢组织和织构的演变  

Evolution of Structure and Texture in 3%Si Steel during Hot and Cold Rolling Process based on CSP Technology

作　　者：闫志飞[1] 金自力[1] 计云萍[1] 刘朋成[1] 张利博[1] 

机构地区：[1]内蒙古科技大学材料与冶金学院,包头014010

出　　处：《特殊钢》2012年第2期65-67,共3页Special Steel

基　　金：内蒙古科技大学创新基金项目(2009NC017)

摘　　要：3%Si钢(/%:0.067C、3.09Si、0.34Mn、0.007P、0.003S、0.70Cu、≤0.005Al、0.0080～0.0120N)由50kg真空感应炉冶炼,并在实验室轧机经6道次热轧成3.5mm板,终轧温度850℃,卷取温度650℃,热轧板经常化处理后由4辊可逆轧机6道次冷轧成0.50mm薄板。分析结果表明,热轧板表面主要为随机分布较大的等轴晶,中心处由细小等轴晶和长条状晶粒组成,并出现了很强的旋转立方织构{001}〈110〉。经过冷轧,薄板表面出现了很强的α织构和γ织构组分,并且冷轧板保留了热轧的{001}〈110〉旋转立方织构。The 3% Si steel （/% ： 0. 067C, 3.09Si, 0. 34Mn, 0. 007P, 0. 003S, 0. 70Cu, 0. 005A1, 0. 008 0 - 0. 012 ON） is melted by a 50 kg vacuum induction furnace and hot rolled to 3.5mm plate by 6 pass with finishing rolling at 850 ℃ and coiling at 650 ℃ by laboratory mill, then normalized hot rolled plate is cold rolled to 0. 5 mm sheet by 4 roll re- versing mill with 6 passes. Analysis results show that at surface region of hot rolled plate there are mainly random distribu- ted larger equiaxial grains, the center area consists of fine equiaxial grains and lath shape grains and the strong rotating cube texture {001} （110） components occur in center area; After cold rolling, the strong ot and y, textures occur at surface region and the hot rolled{001} 〈110〉 rotating cube textures are retained in cold rolled sheet.

关 键 词：3%Si钢热轧冷轧组织织构演变 

分 类 号：TG335.1[金属学及工艺—金属压力加工]