Spectroscopic properties in Er^(3+)/Yb^(3+) Co-doped fluorophosphate glass  

作　　者：郑涛 秦杰明 蒋大勇 吕景文 肖生春 

机构地区：[1]Department of Material Science and Engineering,Changchun University of Science and Technology,Changchun 130022,China

出　　处：《Chinese Physics B》2012年第4期234-239,共6页中国物理B（英文版）

基　　金：supported by the National Natural Science Foundation of China (Grant No. 11075026)

摘　　要：Using the technique of high-temperature melting, a new Er3＋/Yb3＋ co-doped fluorophosphate glass was prepared. The absorption and fluorescence spectra were investigated in depth. The effect of Er3＋ and Yb3＋ concentration on the spectroscopic properties of the glass sample was also discussed. According to the Judd Ofelt theory, the oscillator strength was computed. The lifetime of 4113/2 level （t-m） of Er3＋ ions was 8.23 ms, and the full width at half maximum of the dominating emission peak was 68 nm at 1.53 μm. The large stimulated emission cross section of the Er3＋ was calculated by the McCumher theory. The spectroscopic properties of Er3＋ ion were compared with those in different glasses. The full width at half maximum and σe are larger than those of other glass hosts, indicating this studied glass may be a potentially useful candidate for high-gain erbium-doped fiber amplifier.Using the technique of high-temperature melting, a new Er3＋/Yb3＋ co-doped fluorophosphate glass was prepared. The absorption and fluorescence spectra were investigated in depth. The effect of Er3＋ and Yb3＋ concentration on the spectroscopic properties of the glass sample was also discussed. According to the Judd Ofelt theory, the oscillator strength was computed. The lifetime of 4113/2 level （t-m） of Er3＋ ions was 8.23 ms, and the full width at half maximum of the dominating emission peak was 68 nm at 1.53 μm. The large stimulated emission cross section of the Er3＋ was calculated by the McCumher theory. The spectroscopic properties of Er3＋ ion were compared with those in different glasses. The full width at half maximum and σe are larger than those of other glass hosts, indicating this studied glass may be a potentially useful candidate for high-gain erbium-doped fiber amplifier.

关 键 词：fluorophosphate glass McCumber theory Judd Ofelt theory fluorescence lifetime 

分 类 号：O482.3[理学—固体物理]