改性条件对阻燃型硬质聚氨酯泡沫塑料性能的影响  

Effect of Modification Conditions on Properties of Rigid Polyurethane Foams

作　　者：周晓谦[1] 任晶鑫[1] 李庆雨[1] 窦睿[1] 

机构地区：[1]辽宁工程技术大学材料科学与工程学院,辽宁阜新123000

出　　处：《中国塑料》2012年第3期71-74,共4页China Plastics

摘　　要：选择阻燃剂三聚氰胺和甲基磷酸二甲酯(DMMP)对硬质聚氨酯泡沫塑料进行阻燃改性,研究了异氰酸酯指数、水、三聚氰胺以及DMMP添加量对硬质聚氨酯泡沫塑料阻燃性能和拉伸强度的影响。结果表明,添加三聚氰胺和DMMP可以提高硬质聚氨酯泡沫塑料的阻燃性能,当三聚氰胺的添加量为25份、DMMP的添加量为25份、异氰酸酯指数为1.15、水添加量为1.5份时,硬质聚氨酯泡沫塑料的综合性能最佳。Melamine and dimethyl methyl phosphate （DMMP） was used as flame retardants for rigid polyurethane foams. The effects of isoeyanate index, the amounts of water, melamine, and DMMP on the flame retardaney and tensile strength of the foams were studied. It was found that when the contents of melamine and DMMP were 25 parts each, water content was 1. 5 parts, isocyanate index was 1.15, the foam provided the optimal comprehensive performance.

关 键 词：硬质聚氨酯泡沫塑料 拉伸性能 阻燃性能 三聚氰胺 甲基磷酸二甲酯 

分 类 号：TQ328.3[化学工程—合成树脂塑料工业]