氧化铝土矿制备聚合氯化铝铁和动力学机理的研究  

Research on the Preparation of Polymeric Aluminum Ferric Chloride with Oxidative Bauxite and Kinetics

作　　者：吴烈善[1] 顾琦玮[1] 钟华辉[1] 邱书辉[1] 吕宏虹[1] 

机构地区：[1]广西大学环境学院,广西南宁530004

出　　处：《非金属矿》2012年第2期5-7,11,共4页Non-Metallic Mines

基　　金：国家"863"计划重大项目课题(2009AA06A416);广西自然科学基金(桂科自728010)

摘　　要：采用氧化铝土矿和盐酸为原料制备聚合氯化铝铁。考察了盐酸用量、反应时间、酸溶温度、盐酸浓度和pH值等因素对絮凝剂性能的影响。并对酸溶溶出规律的动力学进行探讨。结果表明:当盐酸用量为45mL、反应时间为120min、酸溶温度为373K、盐酸浓度为5.4mol/L、聚合pH值为3时,产品的盐基度达46.26%,有效成分达9.94%。当反应温度为373 K时,酸溶反应符合动力学四级反应方程:c=(3×10-8t+5.8×10-8)-1/3,其中k=10-8(g/L)-3.h-1。The polymeric aluminum ferric chloride was prepared using oxidative bauxite and hydrochloric acid,and then the factors of the HCl dosage,the reaction time,the reaction temperature,the HCl concentration and pH value were discussed.In addition,the dissolving dynamics was investigated.The results showed that the basicity and efficiency content of product could be up to 46.26% and 9.94% respectively based on the optimum condition,which was the HCl dosage of 45 mL,the reaction time of 120 min,the reaction temperature of 373 K,the HCl concentration of 5.4 mol/L and pH value of 3.Then the acid-soluble was a fourth order reaction： c=（3×10-8t＋5.8×10-8）-1/3at 373 K,and the constant was k=10-8（g/L）-3.h-1.

关 键 词：聚合氯化铝铁 酸溶实验 聚合实验 动力学 

分 类 号：TQ424[化学工程] TD985[矿业工程—选矿]