具有特殊相互作用的聚合物共混物在选择性溶剂中的自组装行为  

The Self - Assembly of Polymer Blends in Selective Solvents

作　　者：袁晓凤[1] 赵汉英[1] 江明[1] 安英丽[2] 

机构地区：[1]复旦大学高分子科学系 [2]南开大学吸附分离功能高分子材料国家重点实验室,天津300071

出　　处：《化学学报》2000年第1期118-121,共4页Acta Chimica Sinica

基　　金：中国博士后科学基金;南开大学吸附分离功能高分子材料国家重点实验室资助

摘　　要：研究了磺化聚苯乙烯(SPS)/聚4-乙烯基吡啶(P4VP)在选择性溶剂甲醇中的自组装行为.用动态光散射的方法考察了P4VP/甲醇初始浓度以及Cu^(2+)的加入对溶液中粒子尺寸的影响,并研究了Cu^(2+)的加入对聚合物溶液粘度的影响.The self- assembly of blends of lightly sulfonated PS (SPS) and P4VP in selective solvents was studied by dynamic light scattering. When SPS/THF solution was added dropwise into excessive P4VP/ methanol solution, stable isolated particles and particle clusters formed as evidenced by the bimodal intensity distribution. The stability of the particles can be attributed to the solvated P4VP chains which are attached to the collapsed SPS chains by the specific interactions. The relationship between the average hydrodynamic diameter of the particles and the initial concentration of the P4VP/methanol solution was studied. Isolated particles and particle clusters were also observed by TEM. The effect of addition of copper ions on the assembly of polymer blends in the solution was also examined. It was found that by adding CuSO4/H2O solution into the SPS/P4VP solution, more particles or clusters were bridged by Cu2+ . The hydrodynamic diameter of the isolated particles and particle clusters increased from 44nm to 90nm, and 146nm to 277nm, respectively, after adding CuSO4/H2O solution into the original solution.

关 键 词：聚合物 自组装 磺化聚苯乙烯 聚4-乙烯基吡啶 

分 类 号：O631[理学—高分子化学]