PA6原位成纤改善PPR的挤出流变性能  

Extrusion Rheological Properties of PPR Modified With In-Situ Fibrillation Composite of PA6

作　　者：孙显茹[1] 宋中心 张昊[1] 吴其晔[1] 

机构地区：[1]青岛科技大学橡塑材料与工程教育部重点实验室,山东青岛266042

出　　处：《现代塑料加工应用》2012年第2期5-8,共4页Modern Plastics Processing and Applications

基　　金：国家自然科学基金资助项目(50973050)

摘　　要：采用原位成纤复合法制备了无规共聚聚丙烯(PPR)/尼龙6(PA6)复合样品,研究了PA6的原位微纤化对PPR熔体挤出流变性能的影响。结果表明,采用的"挤出-热拉伸-淬冷"工艺可实现PA6在PPR基体中的原位微纤化;少量PA6对PPR的挤出螺纹畸变有改善效果;添加相容剂PP-g-MAH(马来酸酐接枝聚丙烯)有利于改善PPR和PA6两相的界面相容性,并明显改善PPR的挤出螺纹畸变。当PA6质量分数为5%时,加入PP-g-MAH后挤出物外观质量较好,出现螺纹畸变的"临界"表观剪切速率从246s-1增大到719s-1。PPR/PA6 composite samples were prepared by in-situ fibrillation method. The influences of in-situ fibrillation of PA6 to the extrusion rheological properties of PPR were studied. The results show that PA6 fibers can be formed in PPR matrix by extrusiomstretehing-quenehing technique. Small quantity of PA6 can modify the helix distortions of PPR extrudates, a little solubilizer PP-g-MAH can modify the interracial compatibility of PPR and PA6, and modify the extrusion helical distortion well. When PA6 is 5% with a little solubilizer, extrusion sample displays better surface quality. Meanwhile, the critical corrected shear rate of the extrusion helical distortion can be increased from 246 s^-1 to 719 s^-1.

关 键 词：无规共聚聚丙烯 尼龙6 原位成纤 流变性能 挤出 螺纹畸变 

分 类 号：TQ327[化学工程—合成树脂塑料工业]