柠檬酸凝胶燃烧法制备Nd^(3+),Yb^(3+):Y_2O_3多晶原料及其相组成和荧光特性的研究  

Phase Composition and Fluorescent Characteristic of Nd^(3+),Yb^(3+):Y_2O_3 Polycrystalline Materials Prepared by Citrate Gel Combustion Method

作　　者：孙晶[1] 王盛男[1] 董彦珉[1] 宋亚娇[1] 李伟行[1] 腾飞[1] 朱鹏[1] 

机构地区：[1]长春理工大学化学与环境工程学院,长春130022

出　　处：《硅酸盐通报》2012年第2期341-344,共4页Bulletin of the Chinese Ceramic Society

摘　　要：本文采用柠檬酸凝胶燃烧法合成了性能优良的Nd3+,Yb3+:Y2O3多晶原料。XRD、IR和SEM测试结果表明样品在900℃煅烧可获得纯相的Nd3+,Yb3+:Y2O3,平均粒径约为40 nm;TG-DTA测试结果表明样品在30～600℃之间失重约为49.28%;从荧光光谱上可以看出两个主要发射峰位于970～1100 nm之间,最强发射峰位于1030nm,对应Yb3+的2F5/2→2F7/2能级跃迁。Nd3＋,Yb3＋：Y2O3 polycrystalline materials were prepared by citrate gel combustion method.XRD,IR and SEM results showed that the best calcining temperature was 900 ℃ when the Nd3＋,Yb3＋：Y2O3 polycrystalline materials were synthesized by citrate-gel-combustion method.And the average diameter was about 40 nm.TG-DTA analysis indicated that the loss ratio was about 49.28% when the temperature changed from 30 ℃ to 600 ℃.Fluorescence spectrum showed that it has two main emission peaks between 970 nm and 1100 nm,and the strongest emission peak was 1030 nm,which was 2F7/2→2F5/2 of Yb3＋.

关 键 词：Nd3+ Yb3+:Y2O3 多晶原料 燃烧法 

分 类 号：O781[理学—晶体学]