S460M钢板TEKKEN焊接试验分析  

Analysis of S460M Steel Plate TEKKEN Weldability Test

作　　者：郭雄华[1] 艾爱国[2] 韩慧仙[1] 沈言锦[3] 

机构地区：[1]湖南机电职业技术学院,湖南长沙410151 [2]湖南华菱湘潭钢铁有限公司,湖南湘潭411101 [3]株洲职业技术学院,湖南株洲412001

出　　处：《热加工工艺》2012年第9期209-210,共2页Hot Working Technology

基　　金：湖南省教育厅科技资助项目(10CO156)

摘　　要：为了分析S460M钢板的焊接性,采用电弧焊分别在室温(26℃)、预热50℃、预热100℃条件下,进行了TEKKEN焊接试验与焊接热影响区最高硬度试验。从试验结果看,在室温、预热50℃、预热100℃条件下焊接试件均无裂纹,而该钢板在预热至100℃时,焊接热影响区最高硬度在328HV左右,冷裂纹倾向不大。试验结果表明,该材料的焊条电弧焊性能好。In order to analyze the weldability of S460M steel plate,S460M steel plate was welded by arc welding method at room temperature（26 ℃）,preheat 50 ℃,preheat 100 ℃,and carried out TEKKEN weldability test and test of maximum hardness in weld heat-affected zone.From the test results,welding specimens have not cracks under the conditions of room temperature,preheat 50℃,preheat 100℃,and when the steel plate is preheated to 100℃,maximum hardness in weld heat-affected zone is about 328 HV and cold crack tendency is little.The results show that the arc welding performance of S460M steel plate is good.

关 键 词：S460M 钢板 焊接性 TEKKEN试验 

分 类 号：TG406[金属学及工艺—焊接]