助磨剂对转炉钢渣的粉磨及性能的影响  

Effect of grinding aids on grinding and performance of steel slag

作　　者：李伟峰[1] 马素花[1,2] 郑娇玲[1] 沈晓冬[1,2] 钟白茜[1] 

机构地区：[1]南京工业大学材料科学与工程学院,江苏南京210009 [2]材料化学工程国家重点实验室,江苏南京210009

出　　处：《混凝土》2012年第4期34-35,40,共3页Concrete

基　　金：国家"973"计划重点基础研究(2009CB623101);江苏省新型环保重点实验室开放基金(AE201008);高等学校博士学科点专项科研基金(20093221120010);江苏省高校自然科学基金(08KJB430006)

摘　　要：从比表面积、筛余、粒度分布等方面研究了5种助磨组分对转炉钢渣粉磨的作用效果,并探讨了助磨组分对钢渣微粉活性、流动度等性能的影响。结果表明:助磨剂对钢渣微粉的粉磨均有一定的助磨作用,80μm筛余显著降低,45μm筛余量变化不明显;同时使初凝时间延长,终凝时间缩短。掺入0.05%酰胺化合物的7、28 d活性指数较空白样增加了8.64%和5.93%。Effect of five kinds of grinding aids on grinding performance of steel slag was studied by determining specific surface area,sieve over-size,particle size distribution.The impact of grinding aids on the performance of steel slag power was also studied.The results show that all grinding aids have good grinding effect on steel slag,and the fineness of 80 μm were decreased.But there was little change with the sieve over size of 45 μm.The initial setting time of samples with grinding aids increased and the final setting time was decreased.The activity index of sample with 0.05% modified amide was increased 8.64% and 5.93% at 7 d and 28 d respectively,compared with sample without grinding aids.

关 键 词：转炉钢渣 钢渣微粉 助磨剂 酰胺化合物 三乙醇胺 

分 类 号：TU528.042[建筑科学—建筑技术科学]