冲击氧化铝单晶中失效波弛豫时间因子的测量  

Observation of relaxation time of the failure wave in impacting the alumina monocrystalline

作　　者：张岱宇[1] 郝高宇[2] 张明建[3] 

机构地区：[1]闽江学院物理学与电子信息工程系,福建福州350108 [2]西南科技大学研究生处,四川绵阳621010 [3]西南交通大学高压物理研究所,四川成都610031

出　　处：《闽江学院学报》2012年第2期35-38,共4页Journal of Minjiang University

基　　金：福建省教育基金B类项目(JB10121);国家自然科学基金(10874141)

摘　　要：在冲击动压为133 GPa的氧化铝单晶的冲击实验中,测量了在850 nm处冲击氧化铝单晶的辐射曲线,发光信号显示被冲击压缩的单晶中存在延迟发射现象;该现象表明氧化铝单晶在冲击波到达后经历了一个再压缩过程,该过程可用失效波解释;通过实验曲线拟合到在133 GPa下失效波的弛豫时间为0.107 ms/cm.The radiance curve of shocked alumina monocrystailine was measured with the radiation pyrom- eter. The experimental pressure is 133 GPa and the dxperimental wavelength is 850 nm. The recorded sig- nals reveal that there is a phenomenon of emission delay in the monocrystalline. It shows a failure wave has been formed in the shocked alumina monocrystalline, the fitted result based on the experimental data demonstrated the formation time of the failure wave in the shocked alumina monoerystalline is 0. 107 microsecond per centimeter.

关 键 词：强冲击 氧化铝单晶 失效波 

分 类 号：O521.3[理学—高压高温物理]