一种陶瓷型壳高温性能研究  

Study on High-Temperature Properties of a Ceramic Shell

作　　者：李民 杜洪强[2,3] 张玲[2] 白雪峰[2] 李雪[2] 

机构地区：[1]空军驻沈阳黎明公司军代表室,辽宁沈阳110043 [2]沈阳黎明航空发动机(集团)有限责任公司,辽宁沈阳110043 [3]沈阳工业大学材料科学与工程学院,辽宁沈阳110870

出　　处：《铸造》2012年第6期610-612,共3页Foundry

摘　　要：采用EC95粉涂料、硅溶胶粘结剂,利用淋砂机涂挂刚玉砂制备了单晶叶片陶瓷型壳,并进行浇注试验。使用强度分析仪、扫描电镜以及X射线衍射仪对陶瓷型壳的高温抗弯强度、高温蠕变特性、型壳高温下的相转变进行了研究。结果表明:随着温度的升高,型壳高温抗弯强度在1 300℃时最低,在1 400℃时最高;浇注试验表明,在1 550℃下,型壳高温抗弯强度大于6.2 MPa才能满足浇注要求。Single crystal blade ceramic shells were made from EC95 powder,silica sol binder,corundum sand stuccoed by sand rain machine.And the ceramic shells were used in casting test.The high temperature bending strength,high temperature creep property and the phase transition of shell in high temperature were studied by use of strength analyzer,SEM,XRD.The results show that with the increase of the temperature,the bending strength of the shell had the lowest value at 1 300 ℃,and the highest value appeared at 1 400 ℃.Casting experiments show that it is the basic requirement of casting that bending strength of shell at 1 550 ℃ is more than 6.2 MPa.

关 键 词：单晶叶片 陶瓷型壳 高温抗弯强度 高温蠕变特性 高温相变 

分 类 号：TQ174.1[化学工程—陶瓷工业]