SYNTHESIS AND PROPERTIES OF SULFONATED POLY(ETHER KETONE)S CONTAINING 3,5-DIMETHYL PHTHALAZINONE MOIETIES AS PROTON EXCHANGE MEMBRANE MATERIALS  

作　　者：蹇锡高 

机构地区：[1]State Key Laboratory of Fine Chemicals,Liaoning High Performance Polymer Engineering Research Center, Liaoning Key Laboratory of Polymer Science and Engineering,School of Chemical Engineering, Dalian University of Technology

出　　处：《Chinese Journal of Polymer Science》2012年第4期511-519,共9页高分子科学（英文版）

基　　金：supported by the Natural Science Foundation of Liaoning Province of China(No.20041076)

摘　　要：Sulfonated poly（ether ketone）s containing 3,5-dimethyl phthalazinone moieties （SPPEK-DMs） with different degrees of sulfonation （DS） were synthesized via direct polycondensation from 4-（3,5-dimethyl-4-hydroxyphenyl）-2,3- phthalazinone, 4,4＇-difluorobenzophenone and 3,3＇-disulfonate-4,4＇-difluorobenzophenone. The chemical structure of SPPEK-DMs was characterized by FTIR and 1H-NMR. Thermal stability of SPPEK-DMs was characterized by the thermogravimetric analysis. The membranes prepared from SPPEK-DMs exhibited ion exchange capacities （IEC） ranging from 0.93 mmol.g-1 to 1.86 mmol.g-1. Water uptake, swelling, oxidative stability and methanol permeability of SPPEK- DMs membranes were investigated. SPPEK-DMs membranes exhibited high oxidative stability. The methanol permeability values of SPPEK-DMs membranes were in the range 5.15× 10^-8-6.61×10^-7 cm^2.s-1, which was much lower than those of Nafion117. The proton conductivity of SPPEK-DM40 membranes was 1.1 ×10^-2 S.cm^-1 at 70℃.Sulfonated poly（ether ketone）s containing 3,5-dimethyl phthalazinone moieties （SPPEK-DMs） with different degrees of sulfonation （DS） were synthesized via direct polycondensation from 4-（3,5-dimethyl-4-hydroxyphenyl）-2,3- phthalazinone, 4,4＇-difluorobenzophenone and 3,3＇-disulfonate-4,4＇-difluorobenzophenone. The chemical structure of SPPEK-DMs was characterized by FTIR and 1H-NMR. Thermal stability of SPPEK-DMs was characterized by the thermogravimetric analysis. The membranes prepared from SPPEK-DMs exhibited ion exchange capacities （IEC） ranging from 0.93 mmol.g-1 to 1.86 mmol.g-1. Water uptake, swelling, oxidative stability and methanol permeability of SPPEK- DMs membranes were investigated. SPPEK-DMs membranes exhibited high oxidative stability. The methanol permeability values of SPPEK-DMs membranes were in the range 5.15× 10^-8-6.61×10^-7 cm^2.s-1, which was much lower than those of Nafion117. The proton conductivity of SPPEK-DM40 membranes was 1.1 ×10^-2 S.cm^-1 at 70℃.

关 键 词：PHTHALAZINONE Sulfonated poly（aryl ether ketone） Proton exchange membrane. 