化学改性高熔体聚丙烯的制备及其挤出发泡特性研究  

Study on the Preparation and Extrusion Foaming Properties of the HMSPP by Chemical Modification

作　　者：胡圣飞[1] 朱贤兵[1] 胡伟[1] 陈祥星[1] 王雄[1] 

机构地区：[1]湖北工业大学化学与环境工程学院,湖北武汉430068

出　　处：《塑料工业》2012年第6期57-60,83,共5页China Plastics Industry

基　　金：湖北省自然科学基金(2009CDB136);湖北省教育厅产学研项目(C2010030)

摘　　要：以过氧化二异丙苯(DCP)为交联剂、三烯丙基异三聚氰酸酯(TAIC)为助交联剂,通过平行双螺杆挤出机制备了高熔体强度聚丙烯(HMSPP),研究了DCP用量对PP的流变性能、材料的热性能及发泡特性的影响。结果表明:DCP与TAIC配合使用能有效控制PP交联,从而制得有一定凝胶含量的HMSPP,同时材料的耐热性也得以提高,当DCP用量为0.8份,TAIC为3份时,制备的HMSPP,挤出发泡特性最佳。The high melt strength polypropylene （HMSPP） was prepared by co-rotating twin-screw ex- truder with dicumyl peroxide （DCP） and triallyl isocyanurate （TAIC） as cross-linking agent and cross-link- ing agent promoter. The effect of the content of DCP on rheological properties, the thermal properties and foa- ming properties were investigated. The results revealed that the HMSPP with a certain gel rate could be ob- tained by the DCP and TAIC synergetic used to effectively control of PP cross-linking. Meanwhile, the heat- resistant performance of HMSPP was also increased. The extrusion foaming properties of the HMSPP was best when the usage of DCP and TAIC were 0. 8 phr and 3 phr respectively.

关 键 词：高熔体强度聚丙烯 过氧化二异丙苯 三烯丙基异三聚氰酸酯 发泡性能 

分 类 号：TQ325.14[化学工程—合成树脂塑料工业]