高性能混凝土抗盐蚀耐久性试验研究  

EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE

作　　者：王明芳[1] 孙玉永[1] 

机构地区：[1]铜陵学院土木建筑系,安徽铜陵244000

出　　处：《工业建筑》2012年第6期127-130,共4页Industrial Construction

基　　金：安徽省高校省级自然科学研究项目(KJ2010B235)

摘　　要：设计4组不同掺量浮石和沸石的高性能混凝土,每组各制作12个试件,其中3个试件用饱和石灰水浸泡2年,3个试件用MgSO4溶液浸泡2年,3个试件用NaCl溶液浸泡2年,然后对它们进行冻融试验,研究高性能混凝土经不同盐溶液侵蚀后质量和抗压强度的变化规律,分析不同矿物掺合料的掺加对高性能混凝土抗盐蚀耐久性的影响。试验结果表明:MgSO4溶液对高性能混凝土的侵蚀破坏能力大于NaCl溶液,掺加浮石和沸石的高性能混凝土抗盐蚀耐久性较强,且沸石掺量越高,抗盐蚀耐久性越强。Four groups of high performance concretes were designed, in which the content of pumice and zeolite was different, and twelve specimens were produced for each group. Three specimens had been eroded in lime saturated water, three in MgSQ solution, and three in NaC1 solution for two years. Then the freezing and thawing experiment on them was done. In the experiment, the change of weight and compressive strength of high performance concrete which had been eroded in different salification solutions was studied, meanwhile, the effects of different mineral admixture on salification erosion resistance durability of high performance concrete were analyzed. The tests results show that MgSO4 solution＇ s erosion of high performance concrete is severer than NaCl solution, besides, salification erosion resistance durability of high performance concrete with pumice and zeolite is good, and it increase with the increase of zeolite content in high performance concrete.

关 键 词：高性能混凝土 盐蚀 耐久性 浮石 沸石 冻融 

分 类 号：TU528[建筑科学—建筑技术科学]