Effects of Warm Deformation on Mechanical Properties of TRIP Aided Fe-C-Mn-Si Multiphase Steel  

作　　者：TIAN Yong LI Zhuan~ 

机构地区：[1]State Key Laboratory of Roiling and Automation, Northeastern University, Shenyang 110004, Liaoning,China [2]Department o{ Material Engineering, Shenyang Institute of Aeronautical Engineering, Shenyang110034, Liaoning, China）

出　　处：《Journal of Iron and Steel Research International》2012年第6期47-52,共6页

基　　金：Sponsored by National Natural Science Foundation of China (50334010)

摘　　要：Warm deformation tests were performed using a kind of tubby heater. The microstructures and mechanical properties of an Fe-C-Mn-Si multiphase steel resulting from different warm deformation temperatures were investiga- ted by using LOM （light optical microscopy）, SEM and XRD. The results indicated that the microstructure contai- ning polygonal ferrite, granular bainite and a significant amount of the stable retained austenite can be obtained through hot deformation and subsequent austempering. Warm deformation temperature affects the mechanical prop- erties of the hot rolled TRIP steels. Ultimate tensile strength balance reached maximum （881 MPa） when the speci- men was deformed at 250 ~C, and the total elongation and strength-ductility reached maximum （38% and 28 614 MPa ~ ~, respectively） at deforming temperature of 100 ~C. Martensite could nucleate when austenite was deformed above M~, because mechanical driving force compensates the decrease of chemical driving force. The TRIP effect occurs in the Fe-C-Mn-Si multiphase steel at deforming temperature ranging from 15 to 350 ~C. The results of the effects of warm deformation on the mechanical properties of the Fe-C-Mn-Si multiphase steel can provide theoretical basis for the ap- plications and the warm working of the hot rolled TRIP sheet steels in industrial manufacturing.Warm deformation tests were performed using a kind of tubby heater. The microstructures and mechanical properties of an Fe-C-Mn-Si multiphase steel resulting from different warm deformation temperatures were investiga- ted by using LOM （light optical microscopy）, SEM and XRD. The results indicated that the microstructure contai- ning polygonal ferrite, granular bainite and a significant amount of the stable retained austenite can be obtained through hot deformation and subsequent austempering. Warm deformation temperature affects the mechanical prop- erties of the hot rolled TRIP steels. Ultimate tensile strength balance reached maximum （881 MPa） when the speci- men was deformed at 250 ~C, and the total elongation and strength-ductility reached maximum （38% and 28 614 MPa ~ ~, respectively） at deforming temperature of 100 ~C. Martensite could nucleate when austenite was deformed above M~, because mechanical driving force compensates the decrease of chemical driving force. The TRIP effect occurs in the Fe-C-Mn-Si multiphase steel at deforming temperature ranging from 15 to 350 ~C. The results of the effects of warm deformation on the mechanical properties of the Fe-C-Mn-Si multiphase steel can provide theoretical basis for the ap- plications and the warm working of the hot rolled TRIP sheet steels in industrial manufacturing.

关 键 词：warm deformation Fe-C-Mn-Si multiphase steel TRIP effect mechanical property 

分 类 号：TG146.21[一般工业技术—材料科学与工程] TN915.04[金属学及工艺—金属材料]